HISTORY
ITEM |
NTN
| HFP |
HSI |
NTA |
NTH |
TEST METHOD |
Tensile Strength |
gf/mm |
MD |
3000↑ |
Sample Size:12.65㎜(Width) x 160㎜(Length) Elongation Speed : 100mm/min Measure Average load and length Elongation=Length Gap x 100(%)
60↑
ITEM
Tensile Strength
gf/mm
MD
3000↑ |
Elongation |
% |
MD |
60↑ |
Sample Size:12.65㎜(Width) x 160㎜(Length) Elongation Speed : 100mm/min Measure Average load and length Elongation=Length Gap x 100(%) |
Heat Shrinkage |
% |
MD |
3.0↓ |
Sample Size : 120㎜(Width) x 120㎜(Length) Oven Temperature : 150℃ x 30min Measure after 30 min in room temperature Measurement Equpment : Optcal Microscope ( x 100)(Reference : JISS-7133 /ASTM D204) |
TD |
1.0↓ |
Bonding Strength ofFilm : Film |
gf/cm |
160±10℃ |
800↑ |
400↑ |
500↑ |
2000↑ |
800↓ |
Method:Heat Seal Test Machine. Lamination roll speed : 100㎜/min Lamination Heating Temperature:160±10℃Pressure:3.0kg/㎠ Pressure time : 1.0 secPeel off Speed : 50±5㎜/min Peel Angle : T-shape |
Bonding Strength ofFilm : Conductor |
gf/mm |
160±10℃ |
50↑ |
40↑ |
50↑ |
40↑ |
50↑ |
Lamination roll speed :100㎜/min Lamination Heating Temperature : 160±10℃ Pressure : 3.0kg/㎠Peel off Speed : 50±5㎜/min Peel Angle : T-shape |
Flammability |
|
|
PASS |
PASS |
PASS |
PASS |
PASS |
Sample Size : 50㎜(Width) x 200㎜(Length)Burning Test.Sample Setting : Set in φ12.7±0.5Open at lower 125mm Flame length : 20㎜Ignition : touch flame for 3 seconds apart below 10mm,re touch flame for 3 seonds Measure time after flame go off. |
UL80℃ equivalent |
|
80℃ |
PASS |
PASS |
PASS |
PASS |
PASS |
Method:Roll laminate Machine laminate Speed:2.0m/min.Pressure:0.3MPa Sample:「Z fold」 Condition:113℃×1Week、 |
UL105℃ equivalent |
|
105℃ |
PASS |
PASS |
PASS |
PASS |
PASS |
VW-1 equivalent |
|
|
PASS |
PASS |
PASS |
PASS |
PASS |
COSMO Method |